Ecological remediation base material prepared from river sediment

doi:10.14088/j.cnki.issn0439-8114.2021.17.013

Abstract

Abstract: The content of organic matter in river sediment is high, which pollutes water body and easily causes secondary pollution. In order to make harmless use of sediment, the river sediment was used as raw materials to prepare the ecological restoration base material, and the preparation technology and performance of the base material were discussed. The results showed that the optimal ratio was cement 5%, sediment 14%, sandy loam 73%, straw pulverized material 2%, water 4% and bacterial liquid 2%. The flexural strength, compressive strength, porosity and water absorption of the ecological remediation base material were 0.65 MPa, 1.185 MPa, 17.46% and 13%, which had certain strength and could be used for slope protection and met the nutritional needs of plant growth.

Key words: sriver sediment, ecological restoration base material, characteristic, slope protection

CLC Number:

TU528

WANG Lan, LI Jia, DAI Qun-wei, GUO Jun, WANG Yan. Ecological remediation base material prepared from river sediment[J]. HUBEI AGRICULTURAL SCIENCES, 2021, 60(17): 66-69.

References

[1] 许炼烽,邓绍龙,陈继鑫,等.河流底泥污染及其控制与修复[J].生态环境学报,2014,23(10):1708-1715.
[2] 熊跃辉. 我国城市黑臭水体成因与防治技术政策[N]. 中国环境报,2015-06-11(02).
[3] 贾云辉. 河道污染底泥修复与处理技术探讨[J].科技资讯,2014,12(4):226-227.
[4] 梁康,杨佘维.河道底泥治理技术研究进展[J].中国资源综合利用,2019,37(6):79-83.
[5] 陈建民,李东灵,肖合顺,等.城市黑臭河道底泥内源污染控制的固化与稳定化技术[J].净水技术,2020,39(8):154-159,166.
[6] 宋淑贞,赵婷婷. 河道底泥处理和处置现状及发展研究[J]. 中国资源综合利用,2019(9):28-30.
[7] 王振雷,桑洛滨,柳志国,等.河道底泥处理技术和资源化利用研究进展[J].广州化工,2019,47(22):41-42,52.
[8] ZHAI Y, WEI X, ZENG G, et al.Study of adsorbent derived from sewage sludge for the removal of Cd²⁺, Ni²⁺ in aqueous solutions[J]. Separation & purification technology,2004,38(2):191-196.
[9] XU G R, ZOU J L, DAI Y.Utilization of dried sludge for making ceramsite.[J]. Water Sci Technol A J Int Assoc Water Pollut Res,2006,54(9):69-79.
[10] 肖光辉.生态混凝土在河道护坡中的应用[J].绿色环保建材,2018(2):245,248.
[11] 马伟芳, 赵新华, 王洪云,等. 排污河道的疏浚底泥在园林中的应用研究[J]. 中国给水排水,2006(23):79-82.
[12] 杨丹, 刘燕, 刘勇. 4种园林植物修复河道疏浚底泥中重金属污染的试验研究[J]. 江苏农业科学, 2018, 46(4):224-227.
[13] 荣浩,李晓凌,岳克栋,等.稻壳调理的底泥基陶粒关键制备技术[J].绿色环保建材,2021(3):23-25,69.
[14] 王可,代群威,邓远明,等.膨润土-污泥基生态混凝土的制备[J].非金属矿,2018,41(5):96-99.
[15] 邵伟. 螯合剂对河道沉积物中重金属的解吸研究[D].太原:太原理工大学, 2015.
[16] 许成凯,裴长春.不同种类有机纤维再生混凝土梁抗裂性能试验研究[J].山西建筑,2016,42(2):109-111.
[17] 于杨格. 胶质类芽孢杆菌胞外聚合物合成的蛋白质组学及絮凝重金属的特征[D].南京:南京师范大学,2019.
[18] XIAO Y J, WANG X J, CHEN W L,et al.Isolation and identification of three potassium-solubilizing bacteria from rape rhizospheric soil and their effects on ryegrass[J]. Taylor & francis,2017,34(10):873-880.
[19] 刘海龙,连宾. 胶质类芽孢杆菌应对过量金离子成矿解毒机制研究[A]. 中国矿物岩石地球化学学会.中国矿物岩石地球化学学会第17届学术年会论文摘要集[C].北京:中国矿物岩石地球化学学会,2019.
[20] 徐方,袁宗征,刘苗,等.有机纤维与聚合物对水泥混凝土层间黏结性能影响研究[J].混凝土,2015(1):90-93.